Membranes formed from aromatic polyarylates

ABSTRACT

The present invention is a class of polymeric membranes formed from aromatic polyarylates derived from dicarboxylic acid chlorides and cardo bisphenols having halo substituents on all portions ortho to the hydroxy functions. These polyarylate membranes exhibit high gas permselectivities and are useful in various gas separation applications.

TECHNICAL FIELD OF THE INVENTION

The present invention relates to polymeric membranes which are useful in gas separation operations.

BACKGROUND OF THE INVENTION

There is a need for improved polymeric materials that are highly permeable, yet may under certain circumstances, provide selective separation of various gas combinations. Such materials would especially be useful in commercial, non-cryogenic gas separation processes.

The commercial application for gas separation devices based on polymeric materials relies, in part, on maximizing the overall gas flux through the membrane. P. H. Kim, et al., J. Appl. Poly. Sci., 34 1761 (1987), reported that the gas flux for a membrane is relatable to the average space between the polymer chains. In addition, they indicated that the density of the polymer is also related to the overall gas flux. The problem, in part, for these commercial applications is to identify polymers with very high flux and with good thermo-mechanical properties. It has generally been observed that to achieve high overall flux requires having a polymer with low chain-chain interactions. This can be exemplified by polymers such as poly(dimethylsiloxane} or poly(4-methyl-1-pentene}. These materials have rather high gas flux values. These high flux materials have, because of their low chain-chain interaction, low glass transition temperatures (Tg). As a consequence, these materials require either special processing conditions to build in chemical and physiochemical crosslinking or they can be used only at rather low application temperatures. By contrast, polymers with strong chain-chain interactions have rather high Tg values and have usually exhibited rather low gas flux. U.S. Pat. Nos. 3,822,202 and 3,899,309; Re 30,351 (1980), disclose a process for separating fluids using a semi-permeable membrane made from polyimides, polyesters or polyamides. The repeating units of the main polymer chain of these membranes are distinguished in that such repeating units have at least one rigid divalent subunit, the two main chain single bonds extending from which are not colinear, is sterically unable to rotate 360° around at least one of these bonds, and has 50% or more of its main chain atoms as members of aromatic rings.

U.S. Pat. No. 4,705,540 discloses a highly permeable aromatic polyimide gas separation membrane and processes for using said membrane. The membrane is an aromatic polyimide membrane in which the phenylenediamines are rigid and are substituted on a essentially all of the positions ortho to the amino substituents, and the acid anhydride groups are essentially all attached to rigid aromatic moieties.

U.S. Pat. Nos. 4,717,393 and 4,717,394 disclose polymeric membranes and processes using the membranes for separating components of a gas mixture. The membranes disclosed in both of these patents are semi-flexible, aromatic polyimides, prepared by polycondensation of dianhydrides with phenylenediamines having alkyl substituents on all ortho positions to the amine functions, Or with mixtures of other, non-alkylated diamines, some components have substituents on all positions ortho to the amine functions. It is taught that the membranes formed from this class of polyimides exhibit improved environmental stability and gas permeability, due to the optimization of the molecular free volume in the polymer.

U.S. Pat. No. 4,378,400 discloses gas separation membranes formed from aromatic polyimides based upon biphenyltetra-carboxylic dianhydride for separating various gas mixtures. Japanese Patent Application 1-194905 discloses gas separation membranes formed from various polyimides and Japanese Patent Applications 63-190607 and 63-278524 disclose gas separation membranes formed from various polyamides. Japanese Patent Application 1-194904 discloses gas separation membranes formed from polyarylates having hydrogen, methyl, or ethyl groups on all positions ortho to the hydroxy functions. Such membranes are reported to have O₂ /N₂ selectivities from 1.7 to 2.5.

U.S. Pat. No. 4,840,646 and related E.P. Application 87303339.3 disclose tetrabromo bisphenol based polyestercarbonate membranes. The bisphenols contain linking groups selected from --C═0--, --SO₂ --, and --0--.

M. Salame in Poly. Eng. Sci., 26 1543 (1986) developed a predictive relationship for oxygen permeability coefficient [(PO₂) ] and polymer structure. In the publication he demonstrates the group contributions of various structural portions of a polymer to P(O₂) values. In particular he indicates the presence of an aromatic group, such as phenyl, in place of a methylene (--CH₂ --) decreases the P(O₂) values for a pair of comparative polymers.

BRIEF SUMMARY OF THE INVENTION

The present invention is a class of improved polyarylate membranes and processes for using said membranes to separate one or more components of a gas mixture. The membranes of the present invention are formed from aromatic polyarylates derived from dicarboxylic acid chlorides and cardo bisphenols having halo substituents on all positions ortho to the hydroxy functions. The subject membranes exhibit exceptionally high gas permselectivity and are useful in gas separation applications, especially for the separation of oxygen and nitrogen from air

DETAILED DESCRIPTION OF THE INVENTION

The present invention is a class of polymeric membranes which exhibit high selectivity in gas separation applications, especially for the separation of oxygen from air. The membranes of the present invention are formed from aromatic polyarylates derived from aromatic dicarboxylic acid chlorides and cardo bisphenols having halo substituents on all positions ortho to the hydroxy functions. The polyarylates from which these membranes are formed can be represented by the structural formula: ##STR1##

Wherein Ar is a C₁ -C₂₀ divalent hydrocarbon, which may be halo substituted, with preferred embodiments being selected from: ##STR2##

R¹ and R² are independently halo, n is an integer greater than 50, and L is: ##STR3## or a multicyclo, preferably bi- or tricyclo, bridging group. In the instances wherein L is a multicyclo bridging group, such group can be represented by the general structural formula: ##STR4## wherein X¹, X², and X³ are independently H or C₁ -C₄ alkyl groups, and X⁴ and X⁵ are independently H or a C₁ -C₄ alkyl group or together form a C₃ -C₁₅ cyclic alkyl group to form a fused ring bridging group. Specific multicyclo bridging groups include: ##STR5##

In the above polymer structure, the presence of halo substituents on all four positions ortho to the hydroxy functionality sterically restricts free rotation around the arylate linkage. It is believed that this rigid intra-molecular conformation may promote greater selectivity for O2 and N2 separation. Membranes formed from the polyarylates disclosed herein exhibit higher gas selectivities (α) than the polyarylate membranes disclosed in Japanese Patent Application 1-194904. In instances where the selectivities of the present membranes are comparable to those of the prior art membranes, the present membranes are distinguishable in that they exhibit significantly higher gas permeabilities.

In addition to the above polyarylate structures, minor amounts of other monomer units may be present which do not affect the gas separation properties of the resultant membranes. The polyarylates of the present invention can be used to form membranes in any desired configuration known in the art, such as dense films, flat sheets, hollow fibers, and the like.

As stated above the polyarylate membranes of the present invention are useful in a variety of gas separation applications, especially for the recovery of oxygen from an O₂ /N₂ stream or from air. The gas mixture to be separated is simply brought into contact with the membrane whereby one or more components selectively permeates through the membrane.

The following examples are presented to better illustrate the present invention and are not meant to be limiting.

EXAMPLE I

Thin film polyarylate membranes were made in accordance with the procedure set out below. These polyarylate membranes had the general structural formula: ##STR6##

MONOMER PREPARATION

A three neck, 500 ml round bottom flask, equipped with a mechanical stirrer, a reflux condenser with N₂ inlet, and an additional funnel, was charged with 40 grams (0.114 moles) of 9,9'bisphenolfluorene, 300 ml of ethanol, and 100 ml of water. The stirring solution was cooled to 0° C. The additional funnel was charged with 25 ml (0.50 moles) . The bromine was added slowly. When the addition was completed the solution was warmed to room temperature and allowed to stir for one hour. The solution was filtered and the was collected and rinsed with water and then dissolved into chloroform and dried over magnesium sulfate. The solution was filtered and some of the chloroform was distilled off. The product slowly crystallized out. The material was recrystallized three times.

POLYMER PREPARATION

All glassware was heated in an oven at ≧120° C. for at least two hours. The glassware was then allowed to cool in a nitrogen atmosphere. Under a nitrogen atmosphere, a three neck 100 mI round bottom flask equipped with a mechanical stirrer and N₂ inlet was charged with 10 grams (0.015 moles) of 9,9'-bis(2,6-dibromophenol) fluorene and 40 ml of anhydrous dimethylacetamide. The solution was warmed to increase monomer solubility. When the monomer had dissolved the solution was cooled to 0° C. 3.05 grams (0.015 moles) isophthaloyl dichloride was added to the stirring solution. Pyridine (8 ml) was also added. The solution's viscosity rapidly increased within the first five minutes. The solution was allowed to stir at room temperature for two hours.

The polymer was worked up by precipitating it in water. The polymer was then redissolved in methylene dichloride and reprecipitated in methanol twice. The resulting white powder was dried under vacuum at 70° C. for twenty-four hours.

FILM TESTING

An 8% polymer solution was prepared in chloroform. The solution was then filtered through a teflon filter to remove particulates. The film was cast on a glass plate. Approximately 10 grams of solution was poured onto the glass plate in a 110 cm glass ring. The solvent was allowed to evaporate off. The film was removed from the plate and dried in a vacuum oven at 100 for twenty four hours, then 250° C. for another 24 hours.

The dried film was placed into a Dow Permeability Cell. A vacuum was pulled on one side and a nitrogen head was on the other. After three days of equilibrating the nitrogen permeability measurement was taken. The system was then purged with oxygen and allowed to equilibrate again before taking the oxygen measurement. The results are as follows:

    P(O.sub.2)=3.5-5.0 barrers

    P(N.sub.2)=0.5-0.75 barrers

    αO.sub.2 /N.sub.2 =6.7-7.0

Additionally, for comparative purposes, a membrane having tetra-methyl instead of tetra-bromo substituents was fabricated in accordance with the above procedures and tested for O2/N2 selectivity. The results of these tests are as follows:

    P(O.sub.2)=7.1 barrers

    P(N.sub.2)=1.25 barrers

    αO.sub.2 N.sub.2 =5.7

As can be seen from these results, the membrane with the tetramethyl substituents performed better than reported in the Japanese Application 1-194904, but still exhibited significantly lower O2/N₂ selectivities than the membrane with the tetra-bromo substituents.

EXAMPLE II

Polyarylate membranes in accordance with the present invention were synthesized which have the general structural formula: ##STR7##

POLYMERIZATION

A one liter, three neck round bottom flask equipped with a mechanical stirrer, reflux condenser, and N₂ dip tube, was charged with 200 ml of water. The water was heated until it refluxed. Nitrogen was bubbled through the solution for one hour. Sodium hydroxide (4 grams, 0.1 mole) was added to the stirring solution. When it had dissolved, the solution was allowed to cool to room temperature. The 4,4'-Norbornylidene-bis-2,6-dibromophenol (30 grams, 0.05 moles) was then added. The monomer dissolved and the solution was allowed to stir for 30 minutes. Benzyltrimethylammonium chloride (0.3 grams) was added as a phase transfer agent. Isophthaloyl dichloride (10 grams, 0.05 moles) was dissolved in 200 ml of methylene dichloride, which was then added to the stirring solution. The solution became viscous. The material was allowed to stir for two hours.

The polymer was worked up by rinsing the solution with a dilute acid solution (1% HCL, 200 ml) , rinsing it with water, and precipitating the polymer in methanol. The polymer was filtered and redissolved in methylene dichloride and reprecipitated in methanol. This procedure was done twice. The resulting white powder was dried under vacuum at 70° C. for 24 hours.

FILM TESTING

An 8% polymer solution in 1,2 dichloroethane was prepared and filtered through a teflon filter to remove particulates. Approximately 10 grams of solution was poured onto the glass plate in a 110 cm glass ring. The solvent was allowed to evaporate off. The film was removed from the plate and dried in a vacuum oven at 100° C. for twenty four hours, then 250° C. for another 48 hours.

The dried film was placed into a Dow Permeability Cell. A vacuum was pulled on one side and a nitrogen head was on the other. After three days of equilibrating the nitrogen permeability measurement was taken. The system was then purged with oxygen and allowed to equilibrate again before taking the oxygen measurement. The results are as follows:

    P(O.sub.2)=2.0 barrers

    P(N.sub.2)=0.25 barrers

    αO.sub.2 /N.sub.2 =7.9

EXAMPLE III

Polyarylate membranes were made in accordance with the present invention having the structural formula: ##STR8##

POLYMERIZATION

A one liter, three neck round bottom flask equipped with a mechanical stirrer, reflux condenser, and N₂ dip tube, was charged with 200 ml of water. The water was heated until it refluxed. Nitrogen was bubbled through the solution for one hour. Sodium hydroxide (4 grams, 0.1 mole) was added to the stirring solution. When it had dissolved, the solution was allowed to cool to room temperature. The 4,4'-Norbornylidene-bis-2,6-dibromophenol (30 grams, 0.05 moles) was then added. The monomer dissolved and the solution was allowed to stir for 30 minutes. Benzyltrimethylammonium chloride (0.3 grams) was added as a phase transfer agent. Terephthaloyl dichloride (10 grams, 0.05 moles) was dissolved in 200 ml of methylene dichloride, which was then added to the stirring solution. The solution became viscous. The material was allowed to stir for two hours.

The polymer was worked up by rinsing the solution with a dilute acid solution (1% HCL, 200 ml) . rinsing it with water, and precipitating the polymer in methanol. The polymer was filtered and redissolved in methylene dichloride and reprecipitated in methanol. This procedure was done twice. The resulting white powder was dried under vacuum at 70° C. for 24 hours.

FILM TESTING

An 8% polymer solution in 1,2 dichloroethane was prepared and filtered through a teflon filter to remove particulates. Approximately 10 grams of solution was poured onto the glass plate in a 110 cm glass ring. The solvent was allowed to evaporate off. The film was removed from the plate and dried in a vacuum oven at 100° C. for twenty four hours, then 250° C. for another 48 hours.

The dried film was placed into a Dow Permeability Cell. A vacuum was pulled on one side and a nitrogen head was on the other. After three days of equilibrating the nitrogen permeability measurement was taken. The system was then purged with oxygen and allowed to equilibrate again before taking the oxygen measurement. The results are as follows:

    P(O.sub.2)=4.5 barrers

    P(N.sub.2)=0.69 barrers

    αO.sub.2 N.sub.2 =6.5

EXAMPLE IV

Thin film polyarylate membranes were made in accordance with the procedure set out below. These polyamide membranes had the general structural formula: ##STR9##

POLYMERIZATION

A one liter, three neck round bottom flask equipped with a mechanical stirrer, reflux condenser, and N₂ dip tube, was charged with 200 ml of water. The water was heated until it refluxed. Nitrogen was bubbled through the solution for one hour. Sodium hydroxide (4 grams, 0.1 mole) was added to the stirring solution. When it had dissolved, the solution was allowed to cool to room temperature. The 4,4'-Norbornylidene-bis-2,6-dibromophenol (30 grams, 0.05 moles) was then added. The monomer dissolved and the solution was allowed to stir for 30 minutes. Benzyltrimethylammonium chloride (0.3 grams) was added as a phase transfer agent. Isophthaloyl dichloride (5 grams, 0.025 moles) and terephthaloyl dichloride (5 grams, 0.025 moles) were dissolved in 200 ml of methylene dichloride, which was then added to the stirring solution. The solution became viscous. The material was allowed to stir for two hours.

The polymer was worked up by rinsing the solution with a dilute acid solution (1% HCL, 200 ml) , rinsing it with water, and precipitating the polymer in methanol. The polymer was filtered and redissolved in methylene dichloride and reprecipitated in methanol. This procedure was done twice. The resulting white powder was dried under vacuum at 70° C. for 24 hours.

FILM TESTING

An 8% polymer solution in 1,2 dichloroethane was prepared and filtered through a teflon filter to remove particulates. Approximately 10 grams of solution was poured onto the glass plate in a 110 cm glass ring. The solvent was allowed to evaporate off. The film was removed from the plate and dried in a vacuum oven at 100° C. for twenty four hours, then 250° C. for another 48 hours.

The dried film was placed into a Dow Permeability Cell. A vacuum was pulled on one side and a nitrogen head was on the other. After three days of equilibrating the nitrogen permeability measurement was taken. The system was then purged with oxygen and allowed to equilibrate again before taking the oxygen measurement. The results are as follows:

    P(O.sub.2)=3.1 barrers

    P(N.sub.2)=0.425 barrers

    αO.sub.2 /N.sub.2 =7.3

Having thus described the present invention, what is now deemed appropriate for Letters Patent is set out in the following appended claims. 

What is claimed is:
 1. A semi-permeable membrane formed from a polyarylate containing polymerizable units of the formula: ##STR10## Wherein Ar is a C₁ -C₂₀ divalent hydrocarbon radical; R¹ and R² are independently halo substituents; n is an integer greater than 50; and L is a multicyclo bridging group or ##STR11##
 2. A membrane in accordance with claim 1 wherein L is ##STR12##
 3. A membrane in accordance with claim 1 wherein Ar is selected from the group consisting of: ##STR13## and mixtures of the above.
 4. A membrane in accordance with claim 1 wherein R¹ and R² are Br.
 5. A membrane in accordance with claim 1 wherein L is a tricyclo bridging group.
 6. A membrane in accordance with claim 1 wherein L is a bicyclo bridging group.
 7. A membrane in accordance with claim 6 wherein L is a bicyclo bridging group having the structural formula: ##STR14##
 8. A membrane in accordance with claim 1 wherein L is a fused ring multicyclo bridging group.
 9. A membrane in accordance with claim 8 wherein said fused ring multicyclo bridging group is selected from the group consisting of: ##STR15##
 10. A process for separating a component of a gas mixture containing at least one other component, said process comprising: bringing said gas mixture into contact with the membrane of claim 1 which is selectively permeable toward one component of said gas mixture, whereby said component selectively permeates through said membrane from a feed side having both a higher partial pressure of said component and a higher total pressure to a permeate side having and a lower partial pressure of said component and a lower total pressure.
 11. A process in accordance with claim 10 wherein the gas mixture is air and oxygen selectively permeates through the membrane.
 12. A process in accordance with claim 10 wherein the gas mixture contains nitrogen and oxygen. 